| About |
|---|
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.155 | g/cm³ | ASTM D792 |
| Liquid | 1.12 | g/cm³ | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 42 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 350 | J/m | ASTM D4812 |
| Charpy Notched Impact Strength | 4.2 | KJ/m² | ISO 179-1 |
| Charpy Unnotch Impact strength | 26 | kJ/m² | ISO 179-1 |
| Drop hammer impact | |||
| 3.2 mm | 0.56 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 130 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 120 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| -60~100℃ | 88 | ppm/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.194 | W/m/K | ASTM C518 |
| specific heat | |||
| 23℃ | 1190 | J/kg/℃ | ASTM E1269 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 4.99E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 18.0 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 3.41 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 7.1E-3 | ASTM D150 | |
| Compared to the leakage tracing index | 600 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 89 | ASTM D2240 | |
| Tensile modulus | |||
| 5 mm/min | 2800 | MPa | ISO 527-2 |
| tensile strength | |||
| 5 mm/min | 82 | MPa | ISO 527-2 |
| Tensile strain | |||
| 5 mm/min | 5.5 | % | ISO 527-2 |
| Bending modulus | 3000 | MPa | ASTM D790-B |
| bending strength | 130 | MPa | ASTM D790-B |
| elongation at break | |||
| 5mm/min | 5.9 | % | ISO 527-2 |
| Taber wear and tear | |||
| CS-17，1 kg | 42 | mg/1000cy | ASTM D4060 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |