| UV STABILIZED PC/ABS ALLOY FOR INJECTION MOULDING APPLICATIONS.&& |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 45 | g/10min | ISO 1133 |
| 240℃，5.0kg | 45 | g/10min | ASTM D1238 |
| Shrinkage rate | 0.40 to 0.70 | % | ISO 2577 |
| MD | 0.40 to 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ASTM D638 |
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 50.0 | MPa | ASTM D638 |
| yield | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 30 | % | ASTM D638 |
| fracture | > 30 | % | ISO 527-2 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| Bending modulus | 2200 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ASTM D790 |
| bending strength | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 450 | J/m | ASTM D256 |
| 23℃ | 35 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 120 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 120 | ℃ | ASTM D1525 |
| Vicat Softening Temp | 120 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 240 to 250 | °C | |
| Barrel front temperature | 250 to 265 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Injection pressure | 70.0 to 100 | MPa | |
| Hold pressure | 35.0 to 70.0 | MPa | |
| Back pressure | 0.350 to 0.700 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |