| PA66，25%玻纤增强 , 注塑级 , 无卤阻燃 , 良好的热稳定性 |
| Product Description | |
|---|---|
| Supplier | Polysyron |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Heat Stabilized,Glass fiber reinforced |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 125 | MPa | ISO 527-1,-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-1/2 |
| bending strength | 185 | MPa | ISO 178-A |
| Bending modulus | 7500 | MPa | ISO 178-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| 10 ℃/min | 260 | ℃ | ISO 11357-1 |
| Hot deformation temperature | |||
| 1.8 MPa | 235 | ℃ | ISO 75-1/2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | Class | UL 94 |
| 0.80 mm | V-0 | Class | UL 94 |
| Igniting temperature of the hot wire | |||
| 2.0 mm | 750 | ℃ | IEC 60695-2 |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 550 | V | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 9 | kJ/m² | ISO 180-1U |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| MD | 0.3-0.5 | % | ISO 294-4 |
| transverse | 0.8-1.0 | % | ISO 294-4 |
| Shrinkage rate | |||
| 60x60x2 mm | |||
| Density | 1.36 | g/cm³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| Processing conditions | Nominal value | Unit | Test method |
| Drying temperature | 100-120 | °C | |
| Drying time | 3-5 | h | |
| Residual moisture | ≤0.1 | % | |
| Injection temperature | 250-285 | °C | |
| Mold temperature | 70-110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |