| About |
|---|
| Acculam® Phenolfab CYBS is a laminate sheet comprised of a phenolic resin binder and woven canvas (cotton) substrate with graphite added to enhance self-lubrication. This material is characterized by good mechanical properties and toughness. It has similarmechanical properties to C/CE. It is not intended for applications needing electrical resistance. It has good machining qualities and good wear resistance&& |
| Product Description | |
|---|---|
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Machinable,Good wear resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr，3.18 mm | < 1.6 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| — | > 85 | J/m | ASTM D256 |
| — | > 75 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Temperature index | 125 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Bond Strength | > 820000 | g |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 105 | ASTM D785 | |
| bending strength | ASTM D790 | ||
| 3.18 mm | > 117 | MPa | ASTM D790 |
| 3.18 mm | > 110 | MPa | ASTM D790 |
| compressive strength | 269 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. CW-A |
| 3. LW-A |
| 4. Flatwise |
| 5. CW |
| 6. LW |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |