| About |
|---|
| Aegis® OXCE is an oxygen scavenging polyamide composition formulated specifically for use in high performance packaging applications where high gas barrier is required. This product is useful in injection and extrusion molding applications. Aegis® OXCE offers high oxygen barrier, even at high humidity, good carbon dioxide barrier, easy processing (particularly in the PET co-injection stretch blow molding process) excellent delamination resistance and clarity.&& |
| Product Description | |
|---|---|
| Supplier | Honeywell |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Block resin |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D1505 |
| Apparent density | 0.75 | g/cm³ | ISO 60 |
| Melt Flow Rate | ISO 1133 | ||
| 260℃，2.16kg | 13 | g/10min | ISO 1133 |
| 280℃，2.16kg | 23 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 90.2 | MPa | ISO 527-2 |
| fracture | 53.7 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 4.4 | % | ISO 527-2 |
| fracture | 130 | % | ISO 527-2 |
| Bending modulus | 2980 | MPa | ISO 178 |
| bending strength | 118 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Carbon dioxide transfer rate | |||
| 23℃，80% RH | 24.8 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen transfer rate | |||
| 23 ℃, 80% RH, cast thin film | < 0.047 | cm³/m²/24 hr | ASTM D3985 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 70.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 62.7 | ℃ | ASTM D648 |
| Glass transition temperature | 74.0 | ℃ | DSC |
| Melting temperature | |||
| DSC | 236 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 80 | °C | |
| Barrel rear temperature | 245 | °C | |
| Barrel middle temperature | 265 | °C | |
| Barrel front temperature | 265 | °C | |
| Nozzle temperature | 265 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Oriented Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |