| About |
|---|
| ALCOM® PC 740/1 PTFE10 is a Polycarbonate (PC) product filled with 10% ptfe fiber. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PC 740/1 PTFE10 include automotive, engineering/industrial parts and housings. Characteristics include: RoHS Compliant Wear Resistant&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good bond |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 55.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 130 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 142 | ℃ | ISO 306 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 100 to 120 | °C | |
| Hot air dryer | 100 to 120 | °C | |
| Drying time | |||
| Desiccant desiccant | 4.0 to 12 | hr | |
| Hot air dryer | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 280 to 320 | °C | |
| Mold temperature | 80 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |