| 3800/LXS is a general purpose ABS with high impact strength. Common Applications: Covers and Housings Vehicle Interiors Vehicle Exteriors with Paint or Korad Marine Parts with Paint or Korad Features and Benefits: Custom color matching Good forming properties Edge trim easily used into future orders Korad can be applied for UV protection High gloss finish&& |
| Product Description | |
|---|---|
| Supplier | Sekisui |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,High impact resistance,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 to 1.04 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 34.5 | MPa | ASTM D638 |
| Bending modulus | 2000 | MPa | ASTM D790 |
| bending strength | 55.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -18℃ | 110 | J/m | ASTM D256 |
| 23℃ | 320 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 85 | ASTM D523 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |