| About |
|---|
| Altuglas® V040 is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Material Status | Commercial: Active |
| Availabilitys | Europe,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 3.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 11 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 1.40 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | |
| 1.8 MPa, unannealed | 101 | ℃ | |
| Vicat Softening Temp | |||
| — | 117 | ℃ | ASTM D1525 3 |
| — | 108 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.50 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 99 | ASTM D785 | |
| tensile strength | |||
| yield | 74.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.0 | % | ASTM D638 |
| Bending modulus | 3240 | MPa | ASTM D790 |
| bending strength | 107 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Processing temperature | Nominal value | Unit | Test method |
| Preheating temperature | 75-90 | ℃ | |
| Preheating time | 3-5 | hr | |
| Nozzle temperature | 230 | ℃ | |
| Front cylinder temperature | 235 | ℃ | |
| Middle cylinder temperature | 230 | ℃ | |
| Rear cylinder temperature | 210 | ℃ | |
| Mold temperature | 65 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 1 (10 N) |
| 3. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |