| TC-1615 A/B is an unfilled, low viscosity laminating resin generally used for fabricating reinforced laminates and bonding all types of pattern boards together. It features an ability to cure at room temperature for applications that do not require a working service temperature above 180°F (82?C). This system can provide service up to 300°F (149?C) when post-cured.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good bond,Room temperature cure |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.02 | g/cm³ | |
| — | 1.15 | g/cm³ | |
| — | 1.19 | g/cm³ | ASTM D792 |
| Specific volume | 0.892 | cm³/g | |
| Water absorption rate | 1.5 | % | ASTM D570 |
| Shrinkage rate | 0.015 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 270 | J/m | ASTM D256 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | |||
| 25℃ | 12.0 to 15.0 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 to 88 | ASTM D2240 | |
| tensile strength | 241 | MPa | ASTM D638 |
| Bending modulus | 15900 | MPa | ASTM D790 |
| bending strength | 279 | MPa | ASTM D790 |
| compressive strength | 290 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 121 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ASTM D3386 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 100, 按容量计算的混合比: 100 | ||
| Component B | 按重量计算的混合比: 15, 按容量计算的混合比: 17 | ||
| Storage period | 52 | wk | |
| Thermosetting mixed viscosity | |||
| 25℃ | 2000 | cP | |
| 25℃ | 1700 | cP | |
| Post curing time | |||
| 25℃ | 16 to 24 | hr | |
| 66℃ | 2.0 | hr | |
| 121℃ | 1.0 | hr | |
| working hours | |||
| 25℃ | 15.0 to 20.0 | hr |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part B, 77°F |
| 3. Part A, 77°F |
| 4. 100 hours |
| 5. Mixed |
| 6. Part A |
| 7. 100 g mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |