| PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Ductility,Good liquidity,High Heat Resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 19 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 24.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2280 | MPa | ASTM D638 |
| Tensile modulus | 2370 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 57.2 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 150 | % | ASTM D638 |
| fracture | 110 | % | ISO 527-2/50 |
| yield | 4.8 | % | ISO 527-2/50 |
| yield | 5.0 | % | ASTM D638 |
| Bending modulus | 2250 | MPa | ISO 178 |
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | 86.0 | MPa | ISO 178 |
| Yield, 50 mm span | 88.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 480 | J/m | ASTM D256 |
| 23℃ | 590 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 34 | kJ/m² | ISO 180-1A |
| 23℃ | 49 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 54.2 | J | ASTM D3763 |
| 23℃，Total Energy | 54.2 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 110 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 113 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 130 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 129 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 105 | ℃ | UL 746 |
| Strength mechanical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 250 to 290 | °C | |
| Barrel middle temperature | 255 to 295 | °C | |
| Barrel front temperature | 260 to 300 | °C | |
| Nozzle temperature | 275 to 300 | °C | |
| Processing (melt) temperature | 275 to 300 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4mm, Cut |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |