CYCOM® E773/E773FR resins are controlled flow epoxy systems with a large processing window. They exhibit excellent high temperature performance up to 180°F (82°C) wet service temperature. The systems have good retention of tack and drape up to 20 days at room temperature in prepreg form. A straight two hour ramp cure in either a press or an autoclave may be used. No post-cure is requirement to achieve service temperature. Suggested Applications: Helicopter blades Other aircraft structural components&&

About

CYCOM® E773/E773FR resins are controlled flow epoxy systems with a large processing window. They exhibit excellent high temperature performance up to 180°F (82°C) wet service temperature. The systems have good retention of tack and drape up to 20 days at room temperature in prepreg form. A straight two hour ramp cure in either a press or an autoclave may be used. No post-cure is requirement to achieve service temperature. Suggested Applications: Helicopter blades Other aircraft structural components&&

Product Description
Supplier	Cytec Industries
Generic	环氧树脂
Material Status	Commercial: Active
Features	High pressure heat resistance
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.28	g/cm³

MECHANICAL	Nominal value	Unit
Tensile modulus
24℃	3450	MPa
tensile strength
24℃	64.1	MPa
Bending modulus	3790	MPa
bending strength	93.8	MPa

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	155	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.