| About |
|---|
| EMERGE ABS 5302 is a black, 20% glass filled ABS which is suitable for use in a wide variety of internal structural component applications in the Information Technology market. This resin exhibits a property balance of flow, rigidity, and dimensional stability. Applications: Information Technology Equipment and consumer electronics Printer internal components Structural frames&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good liquidity,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 1.6 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.15 to 0.25 | % | ASTM D955 |
| TD | 0.35 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 70.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 70.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 2.0 | % | ASTM D638 |
| Fracture, 3.20 mm, injection molded | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 6350 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 114 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 72 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 105 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 100 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| — | 115 | ℃ | ASTM D1525 3 |
| — | 106 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-30~29℃ | 9.0E-5 | 1/℃ | ASTM D696 |
| TD：-30~29℃ | 9.4E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.0 mm，BK，NC，GY | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |