| About |
|---|
| EMPILON® 5 series compound contains an average Tensile Strength property. EMPILON® 5 series can be applied in many fields of use, such as: hand grips, household goods, sporting goods, stationary, toys etc. Styrenic Block Copolyrner is the main content of this 5 series compound, its hardness range is from Shore A 29 ~ Shore D 51. They can be processed by ordinary plastic Injection machinery, extrusion or calendaring etc.&& |
| Product Description | |
|---|---|
| Supplier | EMPILON |
| Generic | SEBS |
| Material Status | Commercial: Active |
| Features | Renewable resources,Hydrolysis stability,Halogen free,No antimony,Block Copolymer,Lead content is low to none,Nontoxicity,Low to no calcium content |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 | % | |
| TD | 0.90 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 73 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 5.79 | MPa | ASTM D412 |
| 300% strain | 3.53 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 360 | % | ASTM D412 |
| Compression deformation | |||
| 23℃，70 hr | 24 | % | ASTM D395 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 125℃，168 hr | -4.0 | % | ASTM D573 |
| The rate of change in ultimate elongation in air | |||
| 125℃，168 hr | -45 | % | ASTM D573 |
| The rate of change in hardness of a hardness tester in the air | |||
| Shaw A, 125 ℃, 168 hr | 11 | ASTM D573 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -55.0 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 165 to 175 | °C | |
| Barrel middle temperature | 175 to 185 | °C | |
| Barrel front temperature | 185 to 195 | °C | |
| Nozzle temperature | 180 to 190 | °C | |
| Processing (melt) temperature | 160 to 200 | °C | |
| Mold temperature | 40 to 50 | °C | |
| Injection pressure | 2.94 to 3.92 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Reference Only |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |