| About |
|---|
| EMPILON® HT series compound has excellent Tensile Strength property, good resilience, low specific gravity, good electrical and mechanical properties. The EMPILON® HT series can be applied in many fields of use, such as: power tool grips, automotive parts, sporting goods etc. Hydrogenated Styrenic Block Copolymer is the main content of this HT series compound, its hardness rangeis from Shore A 28 ~ Shore D 41. They can be processed by ordinary plasticmachinery for Injection, extrusion or calendaring etc.&& |
| Product Description | |
|---|---|
| Supplier | EMPILON |
| Generic | SEBS |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Renewable resources,Hydrolysis stability,Halogen free,No antimony,Block Copolymer,Elastic,Good Tensile Strength,Low density,Lead content is low to none,Nontoxicity,Low to no calcium content |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 29 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 | % | |
| TD | 0.90 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 60 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 8.24 | MPa | ASTM D412 |
| 300% strain | 2.65 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 730 | % | ASTM D412 |
| Compression deformation | |||
| 23℃，70 hr | 21 | % | ASTM D395 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 125℃，168 hr | -11 | % | ASTM D573 |
| The rate of change in ultimate elongation in air | |||
| 125℃，168 hr | -3.0 | % | ASTM D573 |
| The rate of change in hardness of a hardness tester in the air | |||
| Shaw A, 125 ℃, 168 hr | 1.0 | ASTM D573 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -50.0 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 175 to 185 | °C | |
| Barrel middle temperature | 185 to 195 | °C | |
| Barrel front temperature | 190 to 205 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Processing (melt) temperature | 180 to 220 | °C | |
| Mold temperature | 40 to 50 | °C | |
| Injection pressure | 3.43 to 4.90 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Reference Only |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |