| About |
|---|
| 15% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate |
| Product Description | |
|---|---|
| Supplier | EnCom |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.80 | % | |
| MD | 0.30 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6140 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 100 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 6410 | MPa | ISO 178 |
| bending strength | 160 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | 6.0 | kJ/m² | |
| 23℃ | 6.2 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -40℃ | 20 | kJ/m² | |
| 23℃ | 32 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 238 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Melting temperature | 254 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.9E-5 | 1/℃ | |
| MD：-40~23℃ | 3.3E-5 | 1/℃ | |
| MD：55~160℃ | 1.9E-5 | 1/℃ | |
| TD | 9.5E-5 | 1/℃ | |
| TD：-40~23℃ | 7.4E-5 | 1/℃ | |
| TD：55~160℃ | 1.3E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 40 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.50 | ||
| Dissipation factor | |||
| 100 Hz | 0.023 | ||
| 1 MHz | 0.012 | ||
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| Flame retardant level | |||
| 0.75 mm | V-0 | ||
| 1.50 mm | 5VA | ||
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Melt Temperature, Optimum | 280 | °C | |
| Mold temperature | 100 to 120 | °C | |
| Mold Temperature, Optimum | 110 | °C | |
| Hold pressure | 80.0 | MPa | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 12 | m/min | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |