| DESCRIPTION: Epocast® 50-A1 Resin/Hardener 946 epoxy laminating system is an unfilled, solvent-free, easy-to-handle material for the manufacture or repair of composite structures as well as for filament winding. Epocast ® 50-A1 resin/Hardener 946 epoxy laminating system is self extinguishing. Epocast ® 50-A1 / Hardener 946 is qualified to BMS 8-201, Type IV, Rev. F. This product is also available in a longer work life version – Epocast ® 50-A1 resin/Hardener 9816 epoxy laminating system.&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Self-extinguishing,Fast Cure |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D792 | ||
| — | 1.05 | g/cm³ | ASTM D792 |
| — | 1.18 | g/cm³ | ASTM D792 |
| — | 1.21 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression modulus | ASTM D695 | ||
| — | 23.6 | MPa | ASTM D695 |
| — | 25.2 | MPa | ASTM D695 |
| — | 27.9 | MPa | ASTM D695 |
| compressive strength | ASTM D695 | ||
| — | 317 | MPa | ASTM D695 |
| — | 333 | MPa | ASTM D695 |
| — | 349 | MPa | ASTM D695 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | FAR 25.853(a | ||
| Burn length | < 152 | mm | |
| Droplet extinction time | 0.0 | hr | |
| Self extinguishing time | 0.0 | hr |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 15 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 7770 | cP | |
| 25℃ | 400 | cP | |
| 25℃ | 2400 | cP |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Hardener |
| 3. Resin |
| 4. Cure 27 days at 77°F |
| 5. Cure 1 day at 77°F + 2 hr. at 150°F |
| 6. Cure 7 days at 77°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |