| About |
|---|
| DESCRIPTION: Epocast® 89537-A/B epoxy syntactic is a two-part system with glass-fiber reinforcement that can be trowelled or extruded into honeycomb core structures for fastener and attachment potting, core splicing and edge reinforcing. The syntactic has a non-sag consistency that allows for vertical application up to 1/2-inch (1 .25cm) thick. Epocast® 89537-A/B epoxy syntactic is self-extinguishing and meets the requirements of BMS 5-28 Type 7, Class 2.&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Self-extinguishing,Low density |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D792 | ||
| — | 0.850 | g/cm³ | ASTM D792 |
| — | 0.900 | g/cm³ | ASTM D792 |
| — | 1.00 | g/cm³ | ASTM D792 |
| viscosity | ASTM D2196 | ||
| — | Paste | ASTM D2196 | |
| — | Soft-paste | ASTM D2196 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression modulus | |||
| — | 3000 | MPa | ASTM D695 |
| — | 3100 | MPa | ASTM D695 |
| compressive strength | ASTM D695 | ||
| — | 58.6 | MPa | ASTM D695 |
| — | 59.3 | MPa | ASTM D695 |
| — | 60.7 | MPa | ASTM D695 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| burn rate | < 25 | mm/min | BMS 5-28 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 19 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 10000 | cP | ASTM D2196 |
| Gelation time | |||
| 100 gms，25℃ | 1.2 | hr | ASTM D2471 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | |||
| 25℃ | 7.0 | day | |
| Tensile Lap Shear – AL/AL | ASTM D1002 | ||
| — | 8.27 | MPa | ASTM D1002 |
| — | 12.4 | MPa | ASTM D1002 |
| — | 1900 | % | ASTM D1002 |
| Weight gain | ASTM D543 | ||
| Distilled water | 0.30 | % | ASTM D543 |
| Mil-M-5606，hydraulic fluid | 0.37 | % | ASTM D543 |
| Monsanto Low Density Hydraulic Test Fluid | 0.48 | % | ASTM D543 |
| TT-S-735 Test Fluid | 0.40 | % | ASTM D543 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Resin |
| 3. System |
| 4. Hardener |
| 5. After Cure #3 |
| 6. After Cure #1 |
| 7. After Cure #2 |
| 8. on immersion – 24 hrs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |