| About |
|---|
| Hostacom TRC 333N is a 20% mineral filled PP compound. Excellent scratch resistance, very low stress whitening and low emissions. High flow, good stiffness/impact balance. High UV-resistance for use in interior trim applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,High liquidity,Low odor,High scratch resistance,High ESCR |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 18 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.90 to 1.1 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 21.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 75 | % | ISO 527-2/50 |
| Bending modulus | |||
| Secant, 23 ℃ | 2000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |