PC/ABS, Maximum Toughness, Low Temperature Impact Strength, Elevated HDT&&

Product Description
Generic	PC+ABS
Material Status	Commercial: Active
Features	Good flexibility,low-temperature impact resistance,HB
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14	g/cm³	ISO 1183
Melt Flow Rate			ASTM D1238
230℃，3.80kg	2.4	g/10min	ASTM D1238
260℃，2.16kg	6.0	g/10min	ASTM D1238
260℃，3.80kg	20	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.50 to 0.70	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	57.0	MPa	ISO 527-2
Tensile strain
fracture	70	%	ISO 527-2
Bending modulus	2340	MPa	ISO 178
bending strength	76.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180
—	50	kJ/m²	ISO 180
-40℃	20	kJ/m²	ISO 180
-20℃	35	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	113	℃	ISO 75-2/A

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.50 mm	HB		UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.