| About |
|---|
| INSULCAST 116 FR is a one to one ratio (weight or volume) epoxy potting and casting compound designed for production use. The convenient mixing ratio of the material makes it ideal for production line mixing as well as automatic dispensing. INSULCAST 116 FR is among the safest epoxy compounds available. It appreciably reduces the risk of eye, skin or respiratory problems generally associated with the use of epoxy compounds.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| Electrical performance | Nominal value | Unit | Test method |
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 4.40 | ASTM D150 | |
| Dissipation factor | |||
| 1 kHz | 0.020 | ASTM D150 | |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | |||
| — | Black | ||
| — | Grey | ||
| Density | |||
| — | 1.45 | g/cm³ | |
| — | 1.50 | g/cm³ | |
| viscosity | |||
| — | 7.2 | Pa·s | ASTM D2393 |
| — | 8.1 | Pa·s | |
| — | 11 | Pa·s | ASTM D2393 |
| Curing time | |||
| 22℃ | 16 to 24 | hr | |
| Gelation time | |||
| 25℃ | 1.8E+2 to 2.4E+2 | min | |
| storage stability | 90 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 | ASTM D2240 | |
| tensile strength | 65.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 8.0 | % | ASTM D638 |
| bending strength | 68.9 | MPa | ASTM D790 |
| compressive strength | 86.2 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.43 | W/m/K | |
| Hot deformation temperature | 70 | ℃ | |
| Operating temperature | 105 | ℃ | |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 1.0 按容量计算的混合比: 1.0 | ||
| Component B | 按重量计算的混合比: 1.0 按容量计算的混合比: 1.0 | ||
| Storage period | |||
| 25℃ | 52 | wk |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part A |
| 3. Part B |
| 4. Mixed |
| 5. 100 gram mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |