| About |
|---|
| Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Halogen free,Flame Characteristics,Copolymer,V-1,V-0,5VA |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.18 | g/cm³ | ASTM D792 |
| — | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.40 to 0.80 | % | Internal Method |
| TD：3.2 mm | 0.40 to 0.80 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| Weathering resistance | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 60 | kJ/m² | ISO 179/1eA |
| 23℃ | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| -50℃ | 590 | J/m | ASTM D256 |
| -30℃ | 680 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| 23℃，6.4mm | 640 | J/m | ASTM D256 |
| -30℃ | 55 | kJ/m² | ISO 180-1A |
| -30℃ | 65 | kJ/m² | ISO 180-4A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| 23℃ | 80 | kJ/m² | ISO 180-4A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1100 | J/m | Internal Method |
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 52.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 134 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 135 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 120 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 124 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 124 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B120 | 142 | ℃ | ASTM D1525 13 , ISO 306/B120 13 |
| B50 | 140 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.7E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.7E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 120 | ℃ | UL 746 |
| Electrical performance | 125 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | ASTM D149 |
| 3.2 mm in oil | 16 | kV/mm | IEC 60243-1 |
| Dissipation factor | |||
| 50 Hz | 2.4E-3 | ASTM D150 | |
| 60 Hz | 2.4E-3 | ASTM D150 | |
| 1 MHz | 8.5E-3 | ASTM D150 , IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 825 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 35 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 90.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2100 | MPa | ASTM D638 |
| — | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 61.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 130 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2070 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| bending strength | |||
| — | 85.0 | MPa | ISO 178 |
| Yield, 50 mm span | 88.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended injection volume | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 271 to 293 | °C | |
| Barrel middle temperature | 282 to 304 | °C | |
| Barrel front temperature | 293 to 316 | °C | |
| Nozzle temperature | 288 to 310 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2,0 in/min |
| 3. Type I, 2,0 in/min |
| 4. 0,051 in/min |
| 5. 0,079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. Double-gated |
| 9. 80*10*3 mm |
| 10. 63.5*12.7*3.2 mm |
| 11. 120*10*4 mm |
| 12. Rate A (50°C/h), Loading 2 (50 N) |
| 13. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |