| About |
|---|
| LOCTITE HYSOL KL G450H epoxy molding compound contains no bromine, antimony or phosphorus flame retardant. This material is designed to achieve JEDEC Level 3 requirements, at 260°C reflow temperature for a QFP package. LOCTITE HYSOL KL G450H meets UL 94 V-0 Flammability at 3.175mm thickness. Product Benefits Green product Low stress High reliability&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Halogen free,No antimony,Baking,Low to no phosphorus content |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.90 | g/cm³ | |
| Spiral flow length | 110 | cm | |
| Water absorption rate | |||
| 85℃，3days，85% RH | 0.17 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 25℃ | 15200 | MPa | |
| bending strength | |||
| 25℃ | 145 | MPa |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 130 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| < 130℃ | 1.0E-5 | cm/cm/℃ | |
| > 130℃ | 6.0E-5 | cm/cm/℃ | |
| Thermal conductivity coefficient | 0.86 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 25 ℃ | 1.9E+16 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Extractable ion content | |||
| Bromide | < 5 | ppm | |
| Chloride | < 10 | ppm | |
| Sodium | < 4 | ppm |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Gelation time | |||
| 175℃ | 0.50 | min | |
| Storage period | |||
| 5℃ | 12 | month |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 347°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |