| About |
|---|
| Low influence from moisture and temperature to measures and electrical properties, compared with PA66. |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Moisture resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，2.16kg | 5.1 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 5.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.50 | % | DIN 16742 |
| Water absorption rate | |||
| 23℃，24hr | < 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3300 | MPa | ISO 527-1-2 |
| Tensile stress | 80.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 140 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 90.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | 120 | ℃ | IEC 60216 |
| Usage temperature – during lifetime maximum. 200 hr | 160 | °C |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 4 mm | > 1.0E+12 | ohms | IEC 60093 |
| insulation resistance | > 1.0E+12 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | |||
| Hot air dryer | 130 | °C | |
| Vacuum dryer | 120 | °C | |
| Drying time | |||
| Hot air dryer | 6.0 to 8.0 | hr | |
| Vacuum dryer | 4.0 to 6.0 | hr | |
| Temperature at the rear of the barrel | 260 to 300 | °C | |
| Temperature in the middle of the barrel | 260 to 300 | °C | |
| Front temperature of material barrel | 260 to 300 | °C | |
| Nozzle temperature | 250 to 290 | °C | |
| Processing (melt) temperature | 280 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |