| About |
|---|
| Lytex 4023 is a flame retarded version of Lytex 9063. Its use should be considered when a high level of flame retardency is required for the molded component.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Flame Characteristics,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.82 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.10 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.080 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 67 | ASTM D2583 | |
| tensile strength | 172 | MPa | ASTM D638 |
| Bending modulus | 15200 | MPa | ASTM D790 |
| bending strength | 414 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 302 | ℃ | ASTM D648 |
| Continuous use temperature | 177 | ℃ | ASTM D794 |
| Storage period | |||
| -12℃ | 26 | wk | |
| stripping time | |||
| 138℃ | 5.0 to 10 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |