NEONIT® SK80 L8G

About
NEONIT® SK80 L8G is a long glass fiber reinforced epoxy molding compound with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding and manufacturing of large commutators.&&

Product Description
Supplier	SBHPP
Generic	环氧树脂
Material Status	Commercial: Active
Availabilitys	Africa & Middle East ,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.79	g/cm³	ISO 1183
Apparent density	0.59	g/cm³	ISO 60
Shrinkage rate	0.11	%	ISO 2577
Water absorption rate
Equilibrium, 23 ℃, 50% RH	0.050	%	ISO 62
Post contraction	-0.020	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	19000	MPa	ISO 527-2
tensile strength	119	MPa	ISO 527-2
Tensile strain
fracture	0.70	%	ISO 527-2
Bending modulus	17000	MPa	ISO 178
bending strength	255	MPa	ISO 178
compressive strength	265	MPa	ISO 604

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	54	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	195	℃	TMA
Linear coefficient of thermal expansion			TMA
MD	1.0E-5	1/℃	TMA
TD	5.7E-5	1/℃	TMA
Thermal conductivity coefficient	0.49	W/m/K	ASTM E1461

Electrical performance	Nominal value	Unit	Test method
Dielectric strength	29	kV/mm	IEC 60243-1
Dissipation factor
23℃，1 MHz	0.019		IEC 60250
Compared to the leakage tracing index	225	V	IEC 60112

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.