| About |
|---|
| Nexxstar 00111 is a copolymer of ethylene and vinyl acetate.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Availabilitys | Latin America,North America,Europe,Africa & Middle East ,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Vinyl acetate content | 7.5 | wt% | ExxonMobil Method |
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16 kg | 0.5 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 100 | ℃ | |
| Vicat Softening Temperature | 80 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| yld，MD | 9.8 | MPa | ASTM D882 |
| yld，TD | 6.5 | MPa | ASTM D882 |
| brk，MD | 34 | MPa | ASTM D882 |
| brk，TD | 29 | MPa | ASTM D882 |
| Elongation at Break | |||
| MD | 200 | % | ASTM D882 |
| TD | 620 | % | ASTM D882 |
| Tensile Modulus | |||
| MD | 110 | MPa | ASTM D882 |
| TD | 130 | MPa | ASTM D882 |
| tear strength | |||
| MD | 190 | g | ASTM D1922 |
| TD | 60 | g | ASTM D1922 |
| Puncture Force | 67 | N | |
| Puncture Energy | 2.8 | J |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart Drop Impact | g | ASTM D1709A |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Gloss | 52 | ASTM D2457 | |
| Haze | 9.4 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Value reported is an estimate based on ExxonMobil’s correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |