| About |
|---|
| Novalloy-S S4230 (type V) is a Polycarbonate + ABS (PC+ABS) material filled with 30% glass fiber. It is available in Asia Pacific. Primary attribute of Novalloy-S S4230 (type V): Flame Rated.&& |
| Product Description | |
|---|---|
| Supplier | Daicel |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | V-0,5VA |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.10 to 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 92.0 | MPa | ISO 527-2 |
| Bending modulus | 7700 | MPa | ISO 178 |
| bending strength | 145 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 123 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 116 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 3.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 1.5 mm | 26 | kV/mm | ASTM D149 |
| Arc resistance | |||
| 3.0 mm | 69.0 | sec | ASTM D495 |
| 3.0 mm | PLC 6 | ASTM D495 | |
| Compared to the resistance to leakage and marking index | |||
| 3.00 mm | PLC 4 | UL 746 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 100 | V | IEC 60112 |
| High Arc Burning Index (HAI) (1.50 mm) | 149 | UL 746 | |
| High Arc Burning Index (HAI) (1.5 mm) | PLC 0 | UL 746 | |
| High voltage arc marking rate (HVTR) (3.00 mm) | 300 | mm/min | UL 746 |
| High voltage arc marking rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot wire ignition (HWI) (1.50 mm) | 150 | sec | UL 746 |
| Hot wire ignition (HWI) (1.5 mm) | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 120 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 200 to 240 | °C | |
| Barrel middle temperature | 220 to 250 | °C | |
| Barrel front temperature | 230 to 260 | °C | |
| Nozzle temperature | 230 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |