| About |
|---|
| NYCOA 2001 is a flexible, high viscosity, impact modified Nylon 6 resin for extrusion processing and injection molding. NYCOA 2001 is a high viscosity resin that features a very high resistance to impact, high melt strength, and exceptional toughness. NYCOA 2001 is recommended for extruded profiles and tubes requiring very good toughness, even at low temperatures. Injection molding applications include safety guards, and soft-touch appliance parts.&& |
| Product Description | |
|---|---|
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,High Viscosity,Good melt strength,Low temperature toughness |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 235℃，1.0kg | 0.52 | g/10min | ASTM D1238 |
| 235℃，5.0kg | 6.5 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.2 | % | ASTM D955 |
| TD | 1.7 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.3 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 67.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| Bending modulus | 1690 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 6.4mm | 850 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 150 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 55.6 | ℃ | ASTM D648 |
| Melting temperature | 218 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 221 to 241 | °C | |
| Barrel middle temperature | 235 to 252 | °C | |
| Barrel front temperature | 246 to 260 | °C | |
| Nozzle temperature | 254 to 266 | °C | |
| Processing (melt) temperature | 249 to 266 | °C | |
| Mold temperature | 77 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |