| About |
|---|
| Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate injection molding compound. It is available in natural and pigmented versions. It exhibits a superb combination of performance properties including high strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability. Applications Petra 130 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Solvent resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | ASTM D792 |
| Density | 1.55 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 95 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 220 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 240 | ℃ | ISO 75-2/B |
| Melting peak temperature | 245 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 245 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 2.3E-5 | 1/℃ | ASTM E831 |
| 0.75 mm | 140 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric strength | 40 | kV/mm | IEC 60243-1 |
| 1.5 mm | 22 | kV/mm | ASTM D149 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.020 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| -40℃ | 10400 | MPa | ISO 527-2 |
| 23℃ | 10200 | MPa | ISO 527-2 |
| 80℃ | 4950 | MPa | ISO 527-2 |
| 120℃ | 2940 | MPa | ISO 527-2 |
| 150℃ | 2360 | MPa | ISO 527-2 |
| tensile strength | ASTM D638 | ||
| Fracture, -40 ℃ | 210 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 155 | MPa | ASTM D638 |
| Fracture, 80 ℃ | 80.0 | MPa | ASTM D638 |
| Fracture, 120 ℃ | 65.0 | MPa | ASTM D638 |
| Fracture, 150 ℃ | 50.0 | MPa | ASTM D638 |
| tensile strength | ISO 527-2 | ||
| Fracture, -40 ℃ | 210 | MPa | ISO 527-2 |
| Fracture, 23 ℃ | 155 | MPa | ISO 527-2 |
| Fracture, 80 ℃ | 80.0 | MPa | ISO 527-2 |
| Fracture, 121 ℃ | 65.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2 |
| Fracture, 23 ℃ | 3.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| -40℃ | 9660 | MPa | ASTM D790 |
| 23℃ | 8970 | MPa | ASTM D790 |
| 65℃ | 6130 | MPa | ASTM D790 |
| 90℃ | 3440 | MPa | ASTM D790 |
| 121℃ | 2830 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| -40℃ | 275 | MPa | ASTM D790 |
| 23℃ | 240 | MPa | ASTM D790 |
| 65℃ | 170 | MPa | ASTM D790 |
| 90℃ | 105 | MPa | ASTM D790 |
| 121℃ | 85.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 100 to 110 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |