| About |
|---|
| Petra 130 FR BK112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. Applications Petra 130 FR BK112 is generally recommended for applications such as electrical housing and bobbins.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.68 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 245 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD | 2.4E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| Flame retardant grade (0.30 mm) | 75.0 | ℃ | UL 746 |
| 1.5 mm | 155 | ℃ | UL 746 |
| 3.0 mm | 155 | ℃ | UL 746 |
| 0.75 mm | 155 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.30 mm | V-0 | UL 94 | |
| 0.75 mm | V-0 5VA | UL 94 | |
| 1.50 mm | V-0 5VA | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Fracture, -40 ℃ | 170 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 125 | MPa | ASTM D638 |
| Fracture, 80 ℃ | 75.0 | MPa | ASTM D638 |
| Fracture, 121 ℃ | 50.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Fracture, -40 ℃ | 1.7 | % | ASTM D638 |
| Fracture, 23 ℃ | 2.0 | % | ASTM D638 |
| Fracture, 80 ℃ | 4.4 | % | ASTM D638 |
| Fracture, 121 ℃ | 5.6 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 9700 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 210 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 100 to 110 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |