Polylink Polymer PBT-11015-GFFR

About
Filled PBT compounds are manufacturedbycom pounding PBT with specially treated choppedglass and modified with additives to make parts withhigh mechanical properties, heat resistance and fire resistance. Excellent flame retardancy. Good resistance to environmental stress-cracking. High heat deflection temperature. Low warpage. Good mould release. Good Mechanical Properties.&&

Product Description
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Low warping,Good stripping performance,Flame Characteristics,High ESCR,V-0
Availabilitys	Africa & Middle East

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50 to 1.58	g/cm³	Internal Method
Moisture content	< 800	ppm	Internal Method

MECHANICAL	Nominal value	Unit	Test method
tensile strength
fracture	78.5 to 88.3	MPa	ASTM D638
Bending modulus	7350 to 7650	MPa	ASTM D790
bending strength	127 to 147	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	46 to 49	J/m	ASTM D256

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	80 to 100	°C
Drying time	2.0 to 4.0	hr
Barrel 1 zone temperature	215	°C
Barrel 2 zone temperature	220	°C
Barrel 3 zone temperature	230	°C
Barrel 4 zone temperature	240	°C
Barrel 5 zone temperature	245	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.