RheTech Thermoplastic Polyolefin FT1055-685UV

About
Thermoplastic Polyolefin, 110K Flexural Modulus, UV Stabilized, Gray.&&

Product Description
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Weather resistance is good
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.928	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	15	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	60		ASTM D2240
tensile strength	17.2	MPa	ASTM D638
Bending modulus	758	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	800	J/m	ASTM D256
Drop hammer impact	20.3	J	ASTM D5420

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	46.1	℃	ASTM D648
0.45 MPa, unannealed	76.7	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	66 to 82	°C
Drying time	1.0 to 2.0	hr
Recommended maximum moisture content	0.050	%
Barrel rear temperature	188 to 216	°C
Barrel middle temperature	193 to 221	°C
Barrel front temperature	199 to 227	°C
Nozzle temperature	204 to 216	°C
Mold temperature	27 to 49	°C
Injection pressure	2.76 to 10.3	MPa
Hold pressure	2.07 to 8.27	MPa
Back pressure	0.345 to 1.03	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.