| About |
|---|
| SABIC® LDPE 2201H1 is a grade with a low level of anti block and a medium level of slip agent (E=erucamide). Blown Film: The grade has a very good draw down ability. Films based on 2201H1 combine toughness with high tear strength, good optical properties and low CoF. Cast Film: Films made from this grade typically show good optical properties, processability and draw down. Application SABIC® LDPE 2201H1 is typically developed for lamination films, high quality carrier bags and high quality packaging films. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good dissection,Optical performance,Low coefficient of friction,Low density,Good tear strength,Low anti-blocking |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.85 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.15 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | |||
| — | 25 | µm | |
| — | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, cast thin film | 140 | MPa | ISO 527-3 |
| TD, 25 µ m, cast thin film | 140 | MPa | ISO 527-3 |
| MD, 50 µ m, blow molded film | 170 | MPa | ISO 527-3 |
| TD, 50 µ m, blow molded film | 170 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 9.00 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 8.00 | MPa | ISO 527-3 |
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| TD, yield, 50 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| MD, fracture, 25 µ m, blow molded film | 24.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 17.0 | MPa | ISO 527-3 |
| MD, fracture, 50 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 20.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, cast thin film | 260 | % | ISO 527-3 |
| TD, fracture, 25 µ m, cast thin film | 580 | % | ISO 527-3 |
| MD, fracture, 50 µ m, blow molded film | > 200 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | > 500 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | ASTM D4272 | ||
| 50 µ m, blow molded | 250 | J/cm | ASTM D4272 |
| Cast thin film: 25.0 µ m | 220 | J/cm | ASTM D4272 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 45 °, 50.0 µ m, blow molded film | 65 | ASTM D2457 | |
| 45 °, 25 µ m, cast thin film | 73 | ASTM D2457 | |
| Haze | ASTM D1003A | ||
| 50 µ m, blow molded film | 6.0 | % | ASTM D1003A |
| 25 µ m, cast thin film | 4.9 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blocking force | |||
| Blow molded film, 50.0 µ m | 50 | g | Internal Method |
| Re blocking – blow molded film (50.0 µ m) | < 5.0 | g | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 45.0 | kN/m | ISO 6383-2 |
| TD，50 µm | 45.0 | kN/m | ISO 6383-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cast Film |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |