| About |
|---|
| Features Tubular resin Good mechanical properties Excellent clarity Excellent gloss Applications Non-slip shrink film Lamination film Blending resin to modify CoF&& |
| Product Description | |
|---|---|
| Supplier | Sasol |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Inoxidizability,Low density |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| tensile strength | |||
| MD, yield, 30 µ m, blow molded film | 9.00 | MPa | |
| TD, yield, 30 µ m, blow molded film | 9.00 | MPa | |
| MD : Break, 1.2 mil, Blown Film | 23.0 | MPa | |
| TD, fracture, 30 µ m, blow molded film | 19.0 | MPa | |
| Tensile strain | |||
| MD : Break, 1.2 mil, Blown Film | 370 | % | |
| TD, fracture, 30 µ m, blow molded film | 560 | % | |
| Drop hammer impact | |||
| 30 µ m, blow molded film | 70 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 30 µ m, blow molded film | 6.0 | g | |
| TD: 30 µ m, blow molded film | 5.0 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 30 µ m, blow molded film | 70 | ASTM D2457 | |
| transparency | |||
| 30.0 µ m, blow molded film | 65.0 | ASTM D1746 | |
| Haze | |||
| 30 µ m, blow molded film | 6.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel temperature | 125 to 140 | °C | |
| Barrel 1 zone temperature | 130 to 145 | °C | |
| Barrel 2 zone temperature | 140 to 155 | °C | |
| Barrel 3 zone temperature | 150 to 165 | °C | |
| Barrel 4 zone temperature | 155 to 170 | °C | |
| Melt temperature | 190 to 210 | °C | |
| Nozzle temperature | 160 to 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |