| About |
|---|
| Skyrol® SM30 is a transparent film with excellent handling characteristics. It is widely used in stamping foil, metallizing, metallic yarn, flexible packaging and adhesive tape applications. SM30 is highly resistant to “neckdown” or creasing caused by high-temperature, high-tension coating operations.&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low shrinkage |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D1505 |
| Shrinkage rate | |||
| MD：190℃，0.012 mm，20 min | 2.9 | % | Internal Method |
| MD：190℃，0.023 mm，20 min | 2.3 | % | ASTM D955 |
| MD：190℃，0.036 mm，20 min | 2.5 | % | ASTM D955 |
| TD：190℃，0.012 mm，20 min | -0.10 | % | Internal Method |
| TD：190℃，0.023 mm，20 min | 0.30 | % | ASTM D955 |
| TD：190℃，0.036 mm，20 min | 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.40 | ASTM D1894 | |
| With oneself – dynamic | 0.40 | ASTM D1894 | |
| With oneself – dynamic | 0.30 | ASTM D1894 | |
| With oneself – static | 0.50 | ASTM D1894 | |
| With oneself – static | 0.40 | ASTM D1894 | |
| With oneself – static | 0.40 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield, 12 µ m | 269 | MPa | ASTM D882 |
| MD, yield, 23 µ m | 255 | MPa | ASTM D882 |
| MD, yield, 36 µ m | 228 | MPa | ASTM D882 |
| TD, yield, 12 µ m | 228 | MPa | ASTM D882 |
| TD, yield, 23 µ m | 241 | MPa | ASTM D882 |
| TD, yield, 36 µ m | 221 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 120 | % | ASTM D882 |
| MD, fracture, 23 µ m | 130 | % | ASTM D882 |
| MD, fracture, 36 µ m | 150 | % | ASTM D882 |
| TD, fracture, 12 µ m | 130 | % | ASTM D882 |
| TD, fracture, 23 µ m | 130 | % | ASTM D882 |
| TD, fracture, 36 µ m | 140 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 12 µm | 164 | ASTM D523 | |
| 23 µm | 163 | ASTM D523 | |
| 36 µm | 161 | ASTM D523 | |
| Transmittance | ASTM D1003 | ||
| 12.0 µm | 90.0 | % | ASTM D1003 |
| 23.0 µm | 90.0 | % | ASTM D1003 |
| 36.0 µm | 89.0 | % | ASTM D1003 |
| Haze | ASTM D1003 | ||
| 12 µm | 3.0 | % | ASTM D1003 |
| 23 µm | 3.6 | % | ASTM D1003 |
| 36 µm | 4.6 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 36 µm |
| 3. 23 µm |
| 4. 12 µm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |