| About |
|---|
| Stretch-Vac 2000 HM from AdvanSix is a pink tinted, high elongation, heat-stabilized blown film produced from modified polyamide resin. It is recommended as a bagging film for advanced composite fabrication where flexibility under adverse atmospheric conditions is essential. It requires fewer pleats than conventional bagging films and has better flex crack resistance. Stretch-Vac 2000 HM is available in sheet, tube and V-sheet in widths ranging from 48″ to 80″. |
| Product Description | |
|---|---|
| Generic | PA Not specified |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good tear strength,Heat Stabilized |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | 88.9 µm | ||
| Secant modulus – MD (blow molded film) | 621 | MPa | ASTM D882 |
| Tensile strength – MD (fracture, blow molded film) | 90.0 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture, blow molded film | 400 | % | ASTM D882 |
| Dosage (88.0 µ m) | 9.92 | m²/kg | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 218 | ℃ | DSC |
| Process Conditions | |||
|---|---|---|---|
| Squeezing instructions | Nominal value | Unit | Test method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |