| About |
|---|
| PM 8375 Phenolic is a two-stage special purpose molding compound. It is especially designed for applications requiring high solder resistance. Typical applications include coil bobbins and switches. JIS Type EG&& |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | JIS K6911 |
| Apparent density | 0.62 | g/cm³ | JIS K6911 |
| Shrinkage rate | |||
| MD: Transfer molding | 0.60 | % | JIS K6911 |
| Water absorption rate | |||
| 24hr | 0.30 | % | JIS K6911 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 85.0 | MPa | JIS K6911 |
| compressive strength | 200 | MPa | JIS K6911 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.7 | kJ/m² | JIS K6911 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 180 | ℃ | JIS K6911 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 11 | kV/mm | JIS K6911 |
| insulation resistance | JIS K6911 | ||
| — | 1.0E+11 | ohms | |
| — | 1.0E+8 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.490 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60 V/sec |
| 3. Before Boiling |
| 4. After Boiling |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |