| About |
|---|
| E 8354A-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Insulation,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.04 | g/cm³ | ASTM D792 |
| Apparent density | 0.80 | g/cm³ | ASTM D1895 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 48hr | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 90.0 | MPa | ASTM D638 |
| Bending modulus | 20000 | MPa | ASTM D790 |
| bending strength | 148 | MPa | ASTM D790 |
| compressive strength | 262 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 34 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 275 | ℃ | ASTM D648-A |
| Linear coefficient of thermal expansion | |||
| MD | 2.2E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | ASTM D149 | ||
| — | 15 | kV/mm | ASTM D149 |
| — | 14 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 4.40 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.015 | ASTM D150 | |
| Arc resistance | 185 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dry, 60 Hz |
| 3. Method A (Short-Time) |
| 4. Method B (Step-by-Step) |
| 5. Wet |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |