| About |
|---|
| Taitarex® 818K is a General Purpose Polystyrene material. It is available in Asia Pacific or North America for extrusion. Important attributes of Taitarex® 818K are: Flame Rated Clarity Good Processability Heat Resistant High Molecular Weight Typical application of Taitarex® 818K : Sheet&& |
| Product Description | |
|---|---|
| Supplier | Taita |
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High molecular weight,Heat Resistance, Good,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D542 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 2.3 | g/10min | ASTM D1238 |
| Residual SM Monomer | 300 | ppm | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃, 3.18 mm | 53.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 0.125 mm | 2.0 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 107 | ℃ | ASTM D1525 4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 2800 µm | 0.50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1/4″x1/2″x5/2″ |
| 3. 3 mm thick |
| 4. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |