| Thermoplastic Elastomer Vulcanized. This TPE-V compound combines the typical performance of a vulcanized elastomer with the easy processing of a thermoplastic compound. Taroprene is totally recyclable and it can be produced in standard grades and in tailor-made grades. Available in natural, black and colored grade.&& |
| Product Description | |
|---|---|
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Renewable resources |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 2.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 85 | ISO 868 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| fracture | 9.80 | MPa | ASTM D412 |
| 100% strain | 4.70 | MPa | ASTM D412 |
| 300% strain | 6.30 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 560 | % | ASTM D412 |
| tear strength | 40.0 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 42 | % | ASTM D395B |
| 100℃，22 hr | 50 | % | ASTM D395B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 175 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |