| About |
|---|
| Provides wide range moldability and Superior cost performance and Expands the possibility of design. Kyocera Chemical’s Phenolic Molding Compounds “TECOLITE” can possible to high cycle molding and excellent stability within a cylinder. Moreover, “TECOLITE” have a wide molding condition and can be found out easily. In the parts, “TECOLITE” have small mold shrinkage factor therefore it is suitable for precision parts. It is especially the best for mass-production parts, such as a non-fuse breaker, various electric parts, and kitchen parts, etc.&& |
| Product Description | |
|---|---|
| Supplier | KYOCERA |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Low contractility,Fast Cure,HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | |
| Shrinkage rate | |||
| MD | 0.70 to 0.90 | % | |
| MD | 1.2 to 1.4 | % | |
| TD | 0.90 to 1.1 | % | |
| Water absorption rate | |||
| balance | < 0.35 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 78.0 to 98.0 | MPa | |
| compressive strength | 216 to 245 | MPa |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 170 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | > 8.0 | kV/mm | |
| insulation resistance | |||
| After boiling | 1.0E+8 to 1.0E+9 | ohms | |
| As Molded | 1.0E+9 to 1.0E+11 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.71 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Injection Molding |
| 3. Compression Molding |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |