| LDF200YZ is a low density polyethylene resin for film extrusion. LDF200YZ has no slip and anti-block additives. LDF200YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2. APPLICATIONS: T-shirt carrier bags, Display packaging, Light duty shrink film Characteristics: Good optical and good mechanical properties.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Optical performance,Low density |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 30 µ m, blow molded film | 206 | MPa | ASTM D882 |
| 1% secant, TD: 30 µ m, blow molded film | 226 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD : Break, 1.2 mil, Blown Film | 26.5 | MPa | ASTM D882 |
| TD, fracture, 30 µ m, blow molded film | 21.6 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD : Break, 1.2 mil, Blown Film | 310 | % | ASTM D882 |
| TD, fracture, 30 µ m, blow molded film | 580 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µ m, blow molded film | 60 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 30 µ m, blow molded film | 180 | g | ASTM D1922 |
| TD: 30 µ m, blow molded film | 120 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 95.0 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µ m, blow molded film | 7.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |