| About |
|---|
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | POM |
| Material Status | Commercial: Active |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1410 | kg/m³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 2.1 | % | ISO 294 |
| TD | 2.1 | % | ISO 294 |
| Water absorption rate | 0.9 | % | ISO 62 |
| Melt index | |||
| 190℃，2.16kg | 7.5 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2600 | MPa | ISO 527 |
| tensile strength | |||
| yield | 62 | MPa | ISO 527 |
| elongation at break | |||
| yield | 9.4 | % | ISO 527 |
| fracture | 27 | % | ISO 527 |
| Tensile creep modulus | |||
| 1 hr | 1800 | MPa | ISO 899 |
| 1000 hr | 1300 | MPa | ISO 899 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6 | kJ/m² | ISO 179 |
| -30℃ | 5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 240 | kJ/m² | ISO 179 |
| -30℃ | 210 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 156 | ℃ | ISO 75 |
| 1.8 MPa | 95 | ℃ | ISO 75 |
| Vicat Softening Temp | |||
| 50℃/hr 50N | 150 | ℃ | ISO 306 |
| Melting temperature | |||
| 10℃/min | 166 | ℃ | ISO 11357 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | m/m/K | ISO 11359 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E+11 | ohm·m | IEC 62631 |
| Surface resistivity | 1E+13 | ohm | IEC 62631-3-2 |
| Insulation strength | 40 | kV/mm | IEC 60243 |
| Dielectric constant | |||
| 100 Hz | 3.8 | IEC 62631-2-1 | |
| 1 MHz | 3.8 | IEC 62631-2-1 | |
| Dissipation factor | |||
| 100 Hz | 0.001 | IEC 62631-2-1 | |
| 1 MHz | 0.005 | IEC 62631-2-1 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.6 mm | HB | UL 94 | |
| 0.8 mm | HB | UL 94 | |
| Extreme oxygen index | 15 | % | ISO 4589 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |