| About |
|---|
| KEY FEATURES UmaPET CO/CI has good transparency, excellent machinability, high gloss and flexibility. One side corona treatment for improvement in adhesion to inks, adhesives and metal in metallization. The film possesses good thermal, mechanical, optical and surface properties along with excellent transparency and dimensional stability. APPLICATIONS The film is designed for use in printing, metallizing, coating and lamination processes widely for flexible packaging applications.&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Good surface appearance,Good Dimensional Stability,Optical performance,Good Printability,Machinable,Good bond,Electroplating |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | ASTM D1204 | ||
| MD：150℃，0.01 mm，30 min | 2.5 | % | |
| MD：150℃，0.012 mm，30 min | 2.5 | % | |
| MD：150℃，0.015 mm，30 min | 2.5 | % | |
| MD：150℃，0.023 mm，30 min | 2.5 | % | |
| TD：150℃，0.01 mm，30 min | 0.40 | % | |
| TD：150℃，0.012 mm，30 min | 0.40 | % | |
| TD：150℃，0.015 mm，30 min | 0.40 | % | |
| TD：150℃，0.023 mm，30 min | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.48 | ||
| With oneself – dynamic | 0.48 | ||
| With oneself – dynamic | 0.48 | ||
| With oneself – dynamic | 0.44 | ||
| With oneself – static | 0.54 | ||
| With oneself – static | 0.54 | ||
| With oneself – static | 0.54 | ||
| With oneself – static | 0.50 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 10 12 15 23 | µm | |
| film thickness | 10, 12, 15, 23 µm | ||
| tensile strength | ASTM D882 | ||
| MD, fracture, 10 µ m | 206 | MPa | |
| MD, fracture, 12 µ m | 206 | MPa | |
| MD, fracture, 15 µ m | 186 | MPa | |
| MD, fracture, 23 µ m | 186 | MPa | |
| TD, fracture, 10 µ m | 216 | MPa | |
| TD, fracture, 12 µ m | 216 | MPa | |
| TD, fracture, 15 µ m | 206 | MPa | |
| TD, fracture, 23 µ m | 206 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 10 µ m | 100 | % | |
| MD, fracture, 12 µ m | 100 | % | |
| MD, fracture, 15 µ m | 100 | % | |
| MD, fracture, 23 µ m | 100 | % | |
| TD, fracture, 10 µ m | 90 | % | |
| TD, fracture, 12 µ m | 90 | % | |
| TD, fracture, 15 µ m | 90 | % | |
| TD, fracture, 23 µ m | 90 | % | |
| dosage | Internal Method | ||
| 10.0 µm | 71.4 | m²/kg | |
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 10 µm | 3.5 | % | |
| 12 µm | 3.5 | % | |
| 15 µm | 3.5 | % | |
| 23 µm | 4.5 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Wetting Tension | ASTM D2578 | ||
| Coated side：10.0 µm | 52 | dyne/cm | |
| Coated side：12.0 µm | 52 | dyne/cm | |
| Coated side：15.0 µm | 52 | dyne/cm | |
| Coated side：23.0 µm | 52 | dyne/cm | |
| Plain side：10.0 µm | 44 | dyne/cm | |
| Plain side：12.0 µm | 44 | dyne/cm | |
| Plain side：15.0 µm | 44 | dyne/cm | |
| Plain side：23.0 µm | 44 | dyne/cm |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |