| Unipren® Elastomers A3 PRTA010 65A IM06S1 UP338是一种苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)材料,。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Unipren® Elastomers A3 PRTA010 65A IM06S1 UP338的主要特性有: 加工性能良好 良好的抗紫外线能力 耐化学品 典型应用领域包括: 工具 家庭应用 生活消费品&& |
| Product Description | |
|---|---|
| Generic | SEBS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Ozone resistance,Solvent resistance,Soft |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 2.0 to 3.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 62 to 68 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| fracture | 7.00 | MPa | ASTM D412 |
| 100% strain | 2.00 | MPa | ASTM D412 |
| 300% strain | 3.00 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | > 600 | % | ASTM D412 |
| tear strength | 40.0 | kN/m | ASTM D624 |
| Compression deformation | |||
| 70℃，22 hr | 55 | % | ASTM D395B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 170 to 190 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |