| About |
|---|
| 15%的玻璃纤维增强，改善了热老化颜色稳定性，表面光泽度高。 烤箱旋钮和手柄，踢脚板，装饰。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, 5 mm/min | 94 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 5 mm/min | 3 | % | ASTM D638 |
| bending strength | |||
| Fracture, 1.30 mm/min with a span of 50 mm | 145.188 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3mm/min，50mm 跨度 | 5169.87 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 23℃ | |||
| No gap | 25 | cm-kgf/cm | ASTM D 4812 |
| Gap | 4 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| Unannealed, 3.2 mm | |||
| 0.45 MPa | 207 | ℃ | ASTM D 648 |
| 1.8MPa | 180 | ℃ | ASTM D 648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5-0.7 | % | Internal Method |
| TD：3.2 mm | 0.7-0.9 | % | Internal Method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |