| About |
|---|
| VALOX™ V9561 resin Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 33.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.050 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-2/5 |
| yield | 125 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/5 |
| yield | 2.0 | % | ISO 527-2/5 |
| Bending modulus | 10800 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 7.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 230 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 225 | ℃ | ISO 306 |
| B120 | 230 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| MD：23~80℃ | 1.9E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40 to 60 | °C | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 90 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |