| VisiJet® SL HiTemp High temperature resistance to 130°C+ (266°F+) Translucent Humidity and chemically resistant with high rigidity Long term stable properties Ideal for under-the-hood component testing&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance,Moisture resistance,Good stability,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.17 | g/cm³ | |
| — | 1.23 | g/cm³ | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 26 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 130 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 57.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| Glass transition temperature | DMA | ||
| — | 62.0 | ℃ | DMA |
| — | 132 | ℃ | DMA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 86 | ||
| Tensile modulus | 3390 | MPa | ASTM D638 |
| tensile strength | 66.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.0 | % | ASTM D638 |
| Bending modulus | 3080 | MPa | ASTM D790 |
| bending strength | 112 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Liquid @ 25 °C |
| 3. Solid @ 25 °C |
| 4. After thermal postcure @ 160 °C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |