| Extremely Low Viscosity, Steam Resistant, Food Grade&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Food contact compliance,Resistance to the steam,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | kJ/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 130 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| 0.750 mm | 130 | ℃ | |
| 3.00 mm | 130 | ℃ | |
| 0.750 mm | 125 | ℃ | |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 125 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 29 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 2.90 | ||
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 6.6E-4 | ||
| 1 MHz | 9.2E-3 | ||
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| Flammability level | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | ||
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 800 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 825 | ℃ | |
| 3 mm | 875 | ℃ | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 70 | ISO 2039-2 | |
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 23.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Limiting Viscosity Number | 43.0 | cm³/g | ISO 1628-4 |
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |